| Engineering Plastics >> Modified PC >> PC系列产品主要型号典型性能表 |
 |
表1
| PC系列产品主要型号典型性能表 |
项目
Item |
试验方法
Test method |
单位
Unit |
牌 号 |
| ASTM |
PC-410 |
PC-FG610 |
PC-FG620 |
PC-FG30 |
PC-FG410 |
PC-FG420 |
PC-E800 |
PC/ABS-037 |
| 物理性能 |
密度
Density |
D792 |
g/cm3 |
1.2 |
1.26 |
1.33 |
1.42 |
1.3 |
1.4 |
1.27 |
1.08 |
吸水率
Water absorption |
D570 |
％ |
0.2～0.4 |
0.15～0.2 |
0.12～0.2 |
0.1～0.15 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
垂直成型收缩率
Moulding shrinkage longiudinal |
D955 |
％ |
0.4 |
0.3 |
0.2 |
0.15 |
0.2 |
0.15 |
0.4 |
0.4 |
平行成型收缩率
Moulding shrinkage transverse |
D955 |
％ |
0.6 |
0.6 |
0.4 |
0.3 |
0.4 |
0.3 |
O.6 |
0.8 |
| 机械性能 |
拉伸强度
Tensile strength |
D638 |
Mpa |
65 |
70 |
100 |
120 |
90 |
110 |
50 |
46 |
断裂伸长率
Elongation |
D638 |
% |
＞60 |
5 |
3 |
3 |
3 |
3 |
20 |
50 |
弯曲强度
Flexural strength |
D790 |
Mpa |
93 |
113 |
150 |
190 |
150 |
190 |
74 |
70 |
弯曲模量
Flexural modulus |
D790 |
Mpa |
255 |
4000 |
5500 |
7050 |
5500 |
7050 |
2700 |
2200 |
IZOD冲击强度 (缺口）
IZOD impact stregth |
D256 |
kJ/m2 |
70 |
10 |
13 |
15 |
8 |
8 |
35 |
45 |
| 热性能 |
热变形温度,
1.82MPa Heat defl ection temperature |
D648 |
℃ |
125 |
135 |
135 |
135 |
135 |
135 |
125 |
95 |
热变形温度,
0.45MPa Heat defl ection temperature |
D648 |
℃ |
140 |
145 |
146 |
148 |
146 |
148 |
140 |
110 |
熔点
Melting Point |
789 |
℃ |
— |
— |
— |
— |
— |
— |
— |
— |
| 燃烧性能 |
阻燃性 |
UL94 |
|
V0 3.0 mm |
V0 3.0 mm |
V0 3.0 mm |
V0 3.0 mm |
V0 |
V0 |
HB |
|
| 电性能 |
体积电阻
Volume resistivity |
IEC60093 |
Ω·m |
＞1016 |
＞1016 |
＞1016 |
＞1016 |
＞1016 |
＞1016 |
＞1016 |
— |
| CTI |
UL-746A |
Volt |
— |
— |
— |
— |
— |
— |
— |
— |
表2
| PC系列产品主要型号典型性能表 |
项目
Item |
试验方法
Test method |
单位
Unit |
牌 号 |
| ASTM |
PC/ABS-055 |
PC/ABS-H055 |
PC/ABS-073 |
PC/ABS-H073 |
PC/ABS-FRL073 |
PC/ABS-FRX073 |
PC/PBT-045 |
| 物理性能 |
密度
Density |
D792 |
g/cm3 |
1.1 |
1.1 |
1.14 |
1.14 |
1.17 |
1.19 |
1.21 |
吸水率
Water absorption |
D570 |
％ |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
0.2～0.4 |
垂直成型收缩率
Moulding shrinkage longiudinal |
D955 |
％ |
0.4 |
0.4 |
0.4 |
0.4 |
0.4 |
0.4 |
0.6 |
平行成型收缩率
Moulding shrinkage transverse |
D955 |
％ |
0.7 |
0.7 |
0.8 |
0.8 |
0.8 |
0.8 |
0.8 |
| 机械性能 |
拉伸强度
Tensile strength |
D638 |
Mpa |
48 |
49 |
56 |
55 |
55 |
55 |
52 |
断裂伸长率
Elongation |
D638 |
% |
30 |
31 |
110 |
100 |
50 |
50 |
＞100 |
弯曲强度
Flexural strength |
D790 |
Mpa |
80 |
80 |
85 |
85 |
85 |
85 |
75 |
弯曲模量
Flexural modulus |
D790 |
Mpa |
2600 |
2700 |
2500 |
2600 |
2800 |
2800 |
2700 |
IZOD冲击强度 (缺口）
IZOD impact stregth |
D256 |
kJ/m2 |
42 |
40 |
55 |
53 |
60 |
40 |
60 |
| 热性能 |
热变形温度,
1.82MPa Heat defl ection temperature |
D648 |
℃ |
98 |
98 |
110 |
110 |
80 |
110 |
90 |
热变形温度,
0.45MPa Heat defl ection temperature |
D648 |
℃ |
118 |
118 |
125 |
125 |
90 |
125 |
113 |
熔点
Melting Point |
789 |
℃ |
— |
— |
— |
— |
— |
— |
— |
| 燃烧性能 |
阻燃性 |
UL94 |
|
|
|
|
|
V0 1.6mm |
V0 1.6mm |
|
| 电性能 |
体积电阻
Volume resistivity |
IEC60093 |
Ω·m |
— |
— |
— |
— |
— |
— |
— |
| CTI |
UL-746A |
Volt |
— |
— |
— |
— |
— |
— |
— |
|
|
|